C 3215-4:2016  

(1) 

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

目 次 

ページ 

序文 ··································································································································· 1 

1 適用範囲························································································································· 1 

2 引用規格························································································································· 2 

3 用語及び定義,試験における一般事項並びに外観 ··································································· 2 

4 寸法······························································································································· 2 

5 導体抵抗························································································································· 2 

6 伸び······························································································································· 2 

7 軟らかさ························································································································· 2 

8 可とう性及び密着性 ·········································································································· 2 

9 耐熱衝撃························································································································· 3 

10 耐軟化 ·························································································································· 3 

11 耐摩耗 ·························································································································· 3 

12 耐溶剤 ·························································································································· 3 

13 絶縁破壊 ······················································································································· 3 

14 均一性 ·························································································································· 4 

15 温度指数 ······················································································································· 4 

16 耐冷媒 ·························································································································· 4 

17 はんだ付け性 ················································································································· 4 

18 融着性 ·························································································································· 4 

19 誘電正接 ······················································································································· 4 

20 耐トランス油 ················································································································· 4 

21 加熱減量 ······················································································································· 4 

22 ピンホール試験 ·············································································································· 5 

23 包装 ····························································································································· 5 

附属書JA(規定)代替特性 ···································································································· 6 

附属書JB(参考)JISと対応国際規格との対比表 ······································································· 8 

C 3215-4:2016  

(2) 

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

まえがき 

この規格は,工業標準化法第12条第1項の規定に基づき,一般社団法人日本電線工業会(JCMA)及び

一般財団法人日本規格協会(JSA)から,工業標準原案を具して日本工業規格を制定すべきとの申出があ

り,日本工業標準調査会の審議を経て,経済産業大臣が制定した日本工業規格である。 

なお,JIS C 3202:2014の規定をJIS C 3215の規格群の附属書に順次移行させることによって,JIS C 

3202:2014は廃止された。 

この規格は,著作権法で保護対象となっている著作物である。 

この規格の一部が,特許権,出願公開後の特許出願又は実用新案権に抵触する可能性があることに注意

を喚起する。経済産業大臣及び日本工業標準調査会は,このような特許権,出願公開後の特許出願及び実

用新案権に関わる確認について,責任はもたない。 

JIS C 3215の規格群には,次に示す部編成がある。 

JIS C 3215-0-1 巻線共通規格−第0-1部:一般特性−エナメル銅線 

JIS C 3215-0-2 巻線共通規格−第0-2部:一般特性−エナメル平角銅線 

JIS C 3215-0-3 巻線共通規格−第0-3部:一般特性−エナメルアルミニウム線 

JIS C 3215-0-4 巻線共通規格−第0-4部:一般特性−ガラス巻平角銅線及びエナメルガラス巻平角銅

線 

JIS C 3215-1 巻線個別規格−第1部:クラス105のポリビニルアセタール銅線 

JIS C 3215-2 巻線個別規格−第2部:クラス130の融着層付きはんだ付け可能ポリウレタン銅線 

JIS C 3215-4 巻線個別規格−第4部:クラス130のはんだ付け可能ポリウレタン銅線 

JIS C 3215-8 巻線個別規格−第8部:クラス180のポリエステルイミド銅線 

JIS C 3215-14 巻線個別規格−第14部:クラス105のポリビニルアセタールアルミニウム線 

JIS C 3215-17 巻線個別規格−第17部:クラス105のポリビニルアセタール平角銅線 

JIS C 3215-31 巻線個別規格−第31部:温度指数180のポリエステル(イミド)塗料焼付ガラス巻平

角銅線及びエナメルガラス巻平角銅線 

JIS C 3215-32 巻線個別規格−第32部:温度指数155のポリエステル(イミド)塗料焼付ガラス巻平

角銅線及びエナメルガラス巻平角銅線 

JIS C 3215-54 巻線個別規格−第54部:クラス155のポリエステル銅線 

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

日本工業規格          JIS 

C 3215-4:2016 

巻線個別規格−第4部:クラス130のはんだ付け 

可能ポリウレタン銅線 

Specifications for particular types of winding wires-Part 4: Solderable 

polyurethane enamelled round copper wire, class 130 

序文 

この規格は,2000年に第3.2版として発行されたIEC 60317-4を基とし,完全整合化に向けた経過措置

として,技術的内容を変更して作成した日本工業規格である。 

この規格の共通規格は,JIS C 3215-0-1:2014である。 

なお,この規格で側線又は点線の下線を施してある箇所は,対応国際規格を変更している事項である。

変更の一覧表にその説明を付けて,附属書JBに示す。また,附属書JAは対応国際規格にはない事項であ

る。 

適用範囲 

この規格は,クラス130のポリウレタン樹脂を主体とした単一被覆層のエナメル銅線(以下,はんだ付

け可能ポリウレタン銅線という。)について規定する。基本的な化学特性が変わらず,かつ,規定する全て

の電線特性を満足する,変性したポリウレタン樹脂にも適用できる。 

注記1 変性した樹脂とは,特性及び適用性を向上させるため,化学的に変性した樹脂又は1種類以

上の添加剤を加えた樹脂のことをいう。 

この規格は,次のサイズ範囲のはんだ付け可能ポリウレタン銅線について規定する。 

− グレード1:0.018 mm以上,2.000 mm以下 

− グレード2:0.020 mm以上,2.000 mm以下 

− 1種:0.100 mm以上,1.500 mm以下 

− 2種:0.020 mm以上,1.000 mm以下 

− 3種:0.020 mm以上,0.600 mm以下 

公称導体径は,JIS C 3215-0-1の箇条4に規定がある。 

この規格では,対応国際規格で引用がない巻線試験方法の規格について,引用すべき規格番号及び適用

箇条を具体的に規定している。 

注記2 この規格の対応国際規格及びその対応の程度を表す記号を,次に示す。 

IEC 60317-4:2000,Specifications for particular types of winding wires−Part 4: Solderable 

polyurethane enamelled round copper wire, class 130(MOD) 

なお,対応の程度を表す記号“MOD”は,ISO/IEC Guide 21-1に基づき,“修正している”

ことを示す。 

C 3215-4:2016  

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

引用規格 

次に掲げる規格は,この規格に引用されることによって,この規格の規定の一部を構成する。これらの

引用規格は,記載の年の版を適用し,その後の改正版(追補を含む。)は適用しない。 

JIS C 3215-0-1:2014 巻線共通規格−第0-1部:一般特性−エナメル銅線 

注記 対応国際規格:IEC 60317-0-1:1990,Specifications for particular types of winding wires−Part 0: 

General requirements−Section 1: Enamelled round copper wire(MOD) 

JIS C 3216-3:2011 巻線試験方法−第3部:機械的特性 

JIS C 3216-4:2011 巻線試験方法−第4部:化学的特性 

JIS C 3216-5:2011 巻線試験方法−第5部:電気的特性 

JIS C 3216-6:2011 巻線試験方法−第6部:熱的特性 

用語及び定義,試験における一般事項並びに外観 

3.1 

用語及び定義 

この規格で用いる主な用語及び定義は,JIS C 3215-0-1の3.1による。 

3.2 

試験における一般事項 

試験における一般事項は,JIS C 3215-0-1の3.2による。ただし,JIS C 3215-0-1とこの規格との間に相

違のある場合は,この規格の規定を優先する。 

クラス130のはんだ付け可能ポリウレタン銅線は,温度指数130以上,かつ,耐熱衝撃温度155 ℃以上

に適合しなければならない。 

注記 温度指数に相当する温度(℃)は,その温度での線の使用を必ずしも推奨するものではない。

推奨する使用温度は,使用機器に含まれる多くの要因に依存する。 

3.3 

外観 

外観は,JIS C 3215-0-1の3.3による。 

寸法 

寸法は,JIS C 3215-0-1の箇条4による。 

導体抵抗 

導体抵抗は,JIS C 3215-0-1の箇条5による。 

伸び 

伸びは,JIS C 3215-0-1の箇条6による。 

軟らかさ 

軟らかさは,JIS C 3215-0-1の箇条7による。 

可とう性及び密着性 

可とう性及び密着性は,JIS C 3215-0-1の箇条8による。剝離試験の計算に用いる定数Kは,150 mmと

する。 

background image

C 3215-4:2016  

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

耐熱衝撃 

耐熱衝撃は,JIS C 3215-0-1の箇条9による。耐熱衝撃の最低試験温度は,155 ℃とする。 

10 耐軟化 

耐軟化は,JIS C 3216-6の箇条4によって試験したとき,170 ℃で2分以内に短絡してはならない。た

だし,受渡当事者間の協定がある場合は,JA.10によってもよい。 

11 耐摩耗 

耐摩耗は,公称導体径0.250 mm以上,2.000 mm以下のはんだ付け可能ポリウレタン銅線に適用する。

JIS C 3216-3の箇条6によって試験したときの最小破壊力は,表1に適合しなければならない。ただし,

受渡当事者間の協定がある場合は,JA.11によってもよい。 

表1−耐摩耗 

公称導体径 

 
 

mm 

グレード1 

グレード2 

最小 

平均破壊力 

3回の試験の中の 

最小破壊力 

最小 

平均破壊力 

3回の試験の中の 

最小破壊力 

0.250 

2.30 

1.95 

4.10 

3.50 

0.280 

2.50 

2.10 

4.40 

3.70 

0.315 

2.70 

2.30 

4.75 

4.00 

0.355 

2.90 

2.50 

5.10 

4.30 

0.400 

3.15 

2.70 

5.45 

4.60 

0.450 

3.40 

2.90 

5.80 

4.90 

0.500 

3.65 

3.10 

6.20 

5.25 

0.560 

3.90 

3.30 

6.65 

5.60 

0.630 

4.20 

3.55 

7.10 

6.00 

0.710 

4.50 

3.80 

7.60 

6.45 

0.800 

4.80 

4.10 

8.10 

6.90 

0.900 

5.20 

4.40 

8.70 

7.40 

1.000 

5.60 

4.75 

9.30 

7.90 

1.120 

6.00 

5.15 

10.0 

8.50 

1.250 

6.50 

5.55 

10.7 

9.10 

1.400 

7.00 

5.95 

11.4 

9.70 

1.600 

7.50 

6.35 

12.2 

10.4 

1.800 

8.00 

6.80 

13.1 

11.1 

2.000 

8.60 

7.30 

14.0 

11.9 

この表に記載のない公称導体径の場合,より大きく最も近い公称導体径の最小破壊
力を適用する。 

12 耐溶剤 

耐溶剤は,JIS C 3215-0-1の箇条12による。 

13 絶縁破壊 

絶縁破壊は,JIS C 3215-0-1の箇条13による。高温での試験温度は,130 ℃とする。 

C 3215-4:2016  

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

14 均一性 

均一性は,JIS C 3215-0-1の箇条14による。 

15 温度指数 

温度指数は,JIS C 3215-0-1の箇条15による。最小温度指数は,130とする。 

16 耐冷媒 

耐冷媒は,適用しない。 

17 はんだ付け性 

はんだ付け性は,JIS C 3216-4の箇条5によって試験したとき,17.1〜17.3に適合しなければならない。

ただし,受渡当事者間の協定がある場合は,JA.17によってもよい。 

17.1 公称導体径0.050 mm以下の場合 

はんだ付け性は,はんだ槽の温度375±5 ℃のときの最大浸せき(漬)時間を2 sとする。 

はんだ付けされた線の表面は,滑らかであり,かつ,皮膜のかす及びはんだのむらがあってはならない。 

17.2 公称導体径0.050 mmを超え0.100 mm以下の場合 

はんだ付け性は,はんだ槽の温度375±5 ℃のときの最大浸せき時間を2 sとする。 

はんだ付けされた線の表面は,滑らかであり,かつ,皮膜のかす及びはんだのむらがあってはならない。 

17.3 公称導体径0.100 mmを超えの場合 

はんだ付け性は,はんだ槽の温度375±5 ℃のときの最大浸せき時間を2 s以上として,公称導体径に次

の倍率を乗じたものとする。 

− グレード1:8 s/mm 

− グレード2:12 s/mm 

はんだ付けされた線の表面は,滑らかであり,かつ,皮膜のかす及びはんだのむらがあってはならない。 

18 融着性 

融着性は,適用しない。 

19 誘電正接 

この試験は,高周波コイルに使用される場合に適用する。誘電正接は,JIS C 3216-5の箇条6に規定す

る高周波発生器の周波数が約1 MHzのとき300×10−4以下とする。 

20 耐トランス油 

耐トランス油は,適用しない。 

21 加熱減量 

加熱減量は,適用しない。 

background image

C 3215-4:2016  

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

22 ピンホール試験 

ピンホール試験は,JIS C 3216-5の箇条7によって試験したとき,表2に適合しなければならない。た

だし,受渡当事者間の協定がある場合は,JA.22によってもよい。 

表2−最大ピンホール個数 

区分 

最大ピンホール個数 

グレード1 

グレード2 

23 包装 

包装は,JIS C 3215-0-1の箇条23による。 

background image

C 3215-4:2016  

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

附属書JA 

(規定) 
代替特性 

この附属書は,本体の対応する箇条を補足するものであり,本体で規定する寸法及び特性に対し,置き

換えて適用が可能な規格値について規定する。 

注記 この附属書で規定する規格値は,この規格をIEC 60317-4に整合させるに当たり,この内容に

よって大きな変更となり市場の混乱が予想される事項について,完全整合化に向けた経過措置

として,従来のJIS C 3202に従った特性値を併記したものである。 

JA.10 耐軟化 

JIS C 3216-6のJA.4によって試験したときの耐軟化温度は,170 ℃以上とする。 

JA.11 耐摩耗 

耐摩耗は,公称導体径0.260 mm以上,1.500 mm以下のはんだ付け可能ポリウレタン銅線に適用する。

JIS C 3216-3の箇条6によって試験したときの最小破壊力は,表JA.1に適合しなければならない。 

最小破壊力が規定に適合しない場合は,更に2本を一組として二組の試験片について再試験を行うこと

ができる。 

表JA.1−耐摩耗 

公称導体径 

 
 

mm 

1種 

2種 

3種 

最小 

平均破壊力 

3回の試験の中の 

最小破壊力 

最小 

平均破壊力 

3回の試験の中の

最小破壊力 

最小 

平均破壊力 

3回の試験の中の 

最小破壊力 

0.260 

3.4 

2.9 

2.4 

2.0 

1.6 

1.3 

0.270 

3.4 

2.9 

2.4 

2.0 

1.6 

1.3 

0.280 

3.4 

2.9 

2.4 

2.0 

1.6 

1.3 

0.290 

3.4 

2.9 

2.4 

2.0 

1.6 

1.3 

0.300 

3.7 

3.1 

2.6 

2.3 

1.9 

1.6 

0.320 

3.8 

3.2 

2.7 

2.3 

1.9 

1.6 

0.350 

3.8 

3.2 

2.7 

2.3 

1.9 

1.6 

0.370 

3.9 

3.3 

2.7 

2.3 

1.9 

1.6 

0.400 

4.2 

3.5 

3.0 

2.6 

2.0 

1.6 

0.450 

4.6 

3.8 

3.1 

2.6 

2.0 

1.7 

0.500 

4.9 

4.2 

3.5 

2.9 

2.3 

2.0 

0.550 

5.0 

4.2 

3.5 

2.9 

2.4 

2.0 

0.600 

5.0 

4.3 

3.5 

3.0 

2.4 

2.0 

0.650 

5.4 

4.6 

3.6 

3.0 

− 

− 

0.700 

5.8 

4.9 

3.9 

3.3 

− 

− 

0.750 

6.1 

5.1 

4.3 

3.6 

− 

− 

0.800 

6.5 

5.5 

4.7 

3.9 

− 

− 

0.850 

6.9 

5.8 

4.7 

3.9 

− 

− 

0.900 

7.3 

6.1 

5.0 

4.2 

− 

− 

0.950 

7.6 

6.4 

5.4 

4.5 

− 

− 

1.000 

8.0 

6.7 

5.4 

4.6 

− 

− 

background image

C 3215-4:2016  

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

表JA.1−耐摩耗(続き) 

公称導体径 

 
 

mm 

1種 

2種 

3種 

最小 

平均破壊力 

3回の試験の中の

最小破壊力 

最小 

平均破壊力 

3回の試験の中の

最小破壊力 

最小 

平均破壊力 

3回の試験の中の 

最小破壊力 

1.100 

8.4 

7.1 

− 

− 

− 

− 

1.200 

8.5 

7.2 

− 

− 

− 

− 

1.300 

8.9 

7.5 

− 

− 

− 

− 

1.400 

9.0 

7.5 

− 

− 

− 

− 

1.500 

9.5 

7.9 

− 

− 

− 

− 

この表に記載のない公称導体径の場合,より大きく最も近い公称導体径の最小破壊力を適用する。 

JA.17 はんだ付け性 

はんだ付け性は,JIS C 3216-4のJA.5によって試験し,はんだ温度が380±5 ℃で表JA.2の時間浸せき

したとき,一様にはんだが付き,かすが残っていてはならない。 

表JA.2−はんだ浸せき条件 

導体径 

mm 

浸せき時間 

超え 

以下 

− 

0.32 

0.32 

0.50 

0.50 

1.0 

1.0 

1.5 

JA.22 ピンホール試験 

ピンホール試験は,JIS C 3216-5の箇条7による。ピンホール個数は,表JA.3に適合しなければならな

い。ピンホール個数が規定値に適合しない場合は,同一巻枠から更に2本をとって再試験を行うことがで

きる。 

表JA.3−最大ピンホール個数 

区分 

最大ピンホール個数 

1種 

2種 

3種 

12 

参考文献 JIS C 3202:2014 エナメル線 

background image

C 3215-4:2016  

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

附属書JB 

(参考) 

JISと対応国際規格との対比表 

JIS C 3215-4:2016 巻線個別規格−第4部:クラス130のはんだ付け可能ポリウ
レタン銅線 

IEC 60317-4:2000,Specifications for particular types of winding wires−Part 4: 
Solderable polyurethane enamelled round copper wire, class 130 

(I)JISの規定 

(II)国際 
規格番号 

(III)国際規格の規定 

(IV)JISと国際規格との技術的差異の箇条ごと
の評価及びその内容 

(V)JISと国際規格との技術的差
異の理由及び今後の対策 

箇条番号 
及び題名 

内容 

箇条 
番号 

内容 

箇条ごと 
の評価 

技術的差異の内容 

1 適用範囲 種別ごとの適用サ

イズ範囲 

JISとほぼ同じ 

追加 

1種,2種及び3種を追加した。 

国内のIEC規格対応状況を勘案
し,経過措置として,適用サイズ
範囲が異なる種別を追加した。次
回見直し時,IEC規格整合化を図
る。 

巻線試験方法の規
格 

− 

追加 

巻線試験方法を規定する規格の規
格番号及び適用箇条を具体的に規
定した。 

規格利用者の利便を図ったもので
あり,対応国際規格との技術的差
異はない。 

10 耐軟化 

10 

JISとほぼ同じ 

選択 

受渡当事者間の協定によって附属
書JAを選択してもよいとした。 

国内のIEC規格対応状況を勘案
し,経過措置としてJIS C 3216-6
のJA.4を用いることができるよ
うにした。次回見直し時,IEC規
格整合化を図る。 

11 耐摩耗 

11 

JISとほぼ同じ 

選択 

受渡当事者間の協定によって附属
書JAを選択してもよいとした。 

国内のIEC規格対応状況を勘案
し,経過措置として1種,2種及
び3種に対する規定を追加し,こ
れを選択肢とした。次回見直し時,
IEC規格整合化を図る。 

17 はんだ
付け性 

17 

JISとほぼ同じ 

選択 

受渡当事者間の協定によって附属
書JAを選択してもよいとした。 

国内のIEC規格対応状況を勘案
し,経過措置としてJIS C 3202の
附属書Bに準じた規格値を追加し
た。次回見直し時,IEC規格整合
化を図る。 

3

C

 3

2

1

5

-4

2

0

1

6

2019年7月1日の法改正により名称が変わりました。まえがきを除き、本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

background image

C 3215-4:2016  

2019年7月1日の法改正により名称が変わりました。まえがきを除き,本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。 

(I)JISの規定 

(II)国際 
規格番号 

(III)国際規格の規定 

(IV)JISと国際規格との技術的差異の箇条ごと
の評価及びその内容 

(V)JISと国際規格との技術的差
異の理由及び今後の対策 

箇条番号 
及び題名 

内容 

箇条 
番号 

内容 

箇条ごと 
の評価 

技術的差異の内容 

22 ピンホ
ール試験 

− 

規定なし 

追加 

箇条22を追加し,規定値を設定し
た。 

JIS C 3202では既に規定されてお
り,実績もあることから,今回新
たに設定した。グレード1及びグ
レード2の規定値は,現在IECで
検討中の数値を記載した。 

− 

規定なし 

選択 

受渡当事者間の協定によって附属
書JAを選択してもよいとした。 

国内のIEC規格対応状況を勘案
し,経過措置として1種,2種及
び3種に対する規定を追加し,こ
れを選択肢とした。次回見直し時,
IEC規格整合化を図る。 

23 包装 

30 

JISとほぼ同じ 

変更 

箇条番号を規格内の序列に合わせ,
23に変更した。 

箇条番号変更は,関連規格と合わ
せ,規格内で整合させた。 

附属書JA
(規定) 

代替特性(耐軟化,
耐摩耗,はんだ付け
性及びピンホール
試験) 

− 

− 

追加 

耐軟化,耐摩耗,はんだ付け性及び
ピンホール試験の代替特性を追加
した。 

国内のIEC規格対応状況を勘案
し,経過措置としてJIS C 3202の
附属書Bに準じた規格値を追加し
た。次回見直し時,IEC規格整合
化を図る。 

JISと国際規格との対応の程度の全体評価:IEC 60317-4:2000,MOD 

注記1 箇条ごとの評価欄の用語の意味は,次による。 

− 追加 ················ 国際規格にない規定項目又は規定内容を追加している。 
− 変更 ················ 国際規格の規定内容を変更している。 
− 選択 ················ 国際規格の規定内容とは異なる規定内容を追加し,それらのいずれかを選択するとしている。 

注記2 JISと国際規格との対応の程度の全体評価欄の記号の意味は,次による。 

− MOD ··············· 国際規格を修正している。 

3

C

 3

2

1

5

-4

2

0

1

6

2019年7月1日の法改正により名称が変わりました。まえがきを除き、本規格中の「日本工業規格」を「日本産業規格」に読み替えてください。